Waterproof Urea Moulding Compound For Tableware Socket Switch Toilet Cover
Production description:
Field of application
Product property
Property | Standard data | Test Methods | Test Results |
Flow(mm) | 140-200 | GB13454-2 | 194 |
Volatile matters | ≤4.0% | GB/T13455 | 3.7% |
Boiling water resistance | GB13454-2 | No mushy | |
Flexural strength ≥Mpa | ≥80 | GB9341 | 85.4 |
Charpy impact strength(notched) kJ/m2 | ≥1.5-2.1 | GB1043 | 2.0 |
Temperature of deflection °C | ≥115 | GB1634 | 118°c |
Water absorption | ≥100 | GB1034 | 86 |
Moulding shrinkage % | 0.6-1.00 | GB13454-2 | 0.7 |
Curing time | 16-28’S |
|
MOQ: | 1Ton |
Price: | Nogotiable |
Standard Packaging: | 25kg PP woven bag with inner waterproof PE film |
Delivery Period: | 15days after be paid |
Supply Capacity: | 6000Ton/ Month |
Waterproof Urea Moulding Compound For Tableware Socket Switch Toilet Cover
Production description:
Field of application
Product property
Property | Standard data | Test Methods | Test Results |
Flow(mm) | 140-200 | GB13454-2 | 194 |
Volatile matters | ≤4.0% | GB/T13455 | 3.7% |
Boiling water resistance | GB13454-2 | No mushy | |
Flexural strength ≥Mpa | ≥80 | GB9341 | 85.4 |
Charpy impact strength(notched) kJ/m2 | ≥1.5-2.1 | GB1043 | 2.0 |
Temperature of deflection °C | ≥115 | GB1634 | 118°c |
Water absorption | ≥100 | GB1034 | 86 |
Moulding shrinkage % | 0.6-1.00 | GB13454-2 | 0.7 |
Curing time | 16-28’S |