|Place of Origin:||jiangxi,China|
|Minimum Order Quantity:||1Ton|
|Packaging Details:||25kg/ Plastic Woven Bags|
|Delivery Time:||15 days after payment comfirmed|
|Payment Terms:||L/C, D/A, D/P, T/T|
|Supply Ability:||10000Ton/Tons per month|
|Other Names:||Amino Plastic Powder||Standard:||GB13455|
|Impact Strength (notch):||1.8 KJ/m2||Solubility In Formaldehyde:||Dissolved In 10 Minutes|
|Mesh Size:||160-201mm||Content:||30% Melamine|
|Kaolin Turbidity Degree:||10||Flow(mm):||194|
GB13455 Urea Moulding Compound,
Amino Plastic Urea Moulding Compound,
Amino Plastic melamine moulding powder
GB13455 0.02Ash Content Urea Moulding Compound With 30% Melamine
The amount of urea-formaldehyde resin used to make plastic products accounts for only about 10% of total production. In the case of low molar formaldehyde and urea prepared urea-formaldehyde resin, and filler (pulp, wood powder), color, lubricant, curing agent, stabilizer (hexamethylenetramine, ammonium carbonate), plasticizer (urea or thiourea) and other components mixed, and then after drying, grinding, ball milling, screening, urea-formaldehyde pressure molding powder. The temperature and pressure of urea-formaldehyde plastics are 140~150℃ and 25~35MPa, and the pressing time varies according to the thickness of the products, generally 10~60min.
The polymer is non-combustible, water resistant, heat resistant, aging resistance, arc resistance, chemical corrosion resistance, with good insulation, gloss and mechanical strength, widely used in wood, plastic, paint, paper, textile and other industries
|Melamine||Premium||Excellent 1||Excellent 2||First class||Second level||Third level|
|Appearance||White powder with small impurities||White powder with more impurities||White powder with a lot of impurities||White powder with a lot of impurities||White powder with a lot of impurities||Light yellow powder|
|Color degree||≤10||≤20 or bluish and greenish||≤20 or bluish and greenish||≤30 or bluish and greenish||≥30||≥50|
The product must be stored under neutral conditions. Linear UF resins can be cured at room temperature with ammonium chloride as curing agent. The molding powder is cured by heating at 130~160℃, and the curing process can be accelerated by accelerators such as zinc sulfate, trimethyl phosphate and diethyl oxalate. Urea-formaldehyde resin is mainly used in the manufacture of molded plastics, household goods and electrical components, and can also be used as board adhesives, paper and fabric sizing, laminating panels, building decorative boards, etc. Because of its light color and easy coloring, products are often rich in color.
Storage of melamine should be stored in a humidity of 30% to 50%, in a relatively dry, ventilated, stored environment,
Note: After opening the package, it should be sealed immediately to avoid the influence of moisture and moisture.
Packing & Delivery
Packing: white bag, content according to customer's request.
Delivery time: 15-25 days after order confirmation, subject to the minimum order quantity.
Payment Terms: T/T, Western Union, Paypal, L/C at sight.
Mode of transportation :FOB/CIF by sea/air, express, etc.
why choose us?
1. Customization can be provided according to needs.
2. Environment-friendly materials, standard production.
3. Timely and considerate service.